At the critical temperature , both of the phases can coexist in a specimen forming
an austenite martensite microstructure. The simplest
austenite martensite microstructure is a homogeneous region
of the austenite phase coexisting with a homogeneous region
of a single variant of the martensite phase. Such a deformation
is depicted in Figure 1 below.
Figure 1: Austenite single variant of martensite microstructure
The compatibility equation for this microstructure with the variant Ui can be written as
The unknowns in the equation above are the rotation
, the shape
strain
, and the
habit plane normal
.
Further, this equation is called the habit plane equation.
The shape strain gives the magnitude and sense of the
transformation; while, the habit plane is the interface
between the two phases. In general, the shape strain does not
lie in the habit plane, and therefore, the transformation involves
both shear and dilatation.
Solutions exists to the habit plane equation if and only if the matrix Ui has an eigenvalue less than one, an eigenvalue equal to one, and an eigenvalue greater than one. This requires special lattice parameters. In any event, at most two solutions can exist to the habit plane equation.
In addition, if solutions exist to the habit plane equation, then they can in general be divided into two sets of symmetry related solutions. The number of solutions in each set is of course the same as the number of martensite variants.
Some of the austenite single variant of martensite microstructures which are possible for the different transitions as listed in the table below.
Austenite Single Variant of Martensite Microstructures |
|||
---|---|---|---|
Transition | Number | Observed | Comment |
Cubic-to-Trigonal | 0 | No | only with ![]() |
Cubic-to-Tetragonal | 3 | No | with ![]() |
Cubic-to-Orthorhombic | 12 | Ti-Ta, Ti-Ni-Cu | with ![]() |
" | 12 | No | with ![]() |
Cubic-to-Monoclinic | 0 | No | not possible with the lattice parameters of Ti-Ni |
In the table above, the first column is the transition; the second lists the number of unique microstructures which can be formed using all of the martensite variants; the third column indicates if the microstructure is observed; and the last column contains some comments.
Another austenite martensite microstructure has twinned martensite and austenite coexisting.